KUH-50

KUH-50
Description


Manual Probes Features

● Perfect Accuracy: ±3% HV, ±1.5HR, ±3%HB

● Microscopic Indentation

● Support 360° quick measuring

● Result in 2 seconds

● Directly display measurement result, times count, maximum, minimal, average and deviation. 

● Save 1000 groups measurement data, Save 20 groups calibration data for invoking, improve calibration efficiency

● Standards: DIN 50159; ASTMA1038 ; JB/T9377


Specifications:

Product Name

Ultrasonic   Hardness Tester

Model

KUH50

Indenter

136°Vickers   Diamond Indenter

Loading Force  

2Kgf(Optional: 1Kgf, 5Kgf, 10Kgf)

Measuring   Range

HB: 85-650;HV   80-1599; HRC 20-70;HRB: 41-100; HRA: 61-85.6

HS:   34.2-97.3;Mpa: 255-2180N/mm

Measuring Accuracy

HV:±3%HV;   HRC:±1.5HRC; HB:±3%HB; HLD:±5HLD;

Measuring Direction

Support 360°

Data Storage

To save 1000-groups of measuring data and 20-groups of calibration data

Hardness Scale

HVHBHRC, HLD

Data Display

Loading force, Testing-times, Testing result, Average, 
    Maximum
MinimumDeviation   and Conversion scale.

Hardness Indication

LCD display

Language Selection

English, German, French, Spanish, Japanese,Turkish  etc.

Operating Environment

Temperature:-10~50;   Humidity: 30%~80%R.H

Recharging Time

Battery Usage

Approx. 8 hours

Approx. 7 hours (no backlight)

Operating Voltage

DC 6V

Instrument Dimensions

160x80x31mm

Net Weight

Approximate 500gWithout probe

1.jpg

Manual Probe Specifications:   


Probe   Type

1Kgf

2Kgf

5Kgf

10Kgf

Remark

Optional

Standard

Optional

Optional

Loading force

10N

20N

50N

98N

Diameter

22mm

22mm

22mm

22mm

Length

154mm

154mm

154mm

154mm

Oscillating Rod   Diameter

2.4mm

2.4mm

3mm

3mm

Roughness of measuring   surface

Ra<3.2um

Ra<5um

Ra<10um

Ra<15um

Min weight of test   material

0.3kg

0.3kg

0.3kg

0.3kg

Min thickness of test   material

2mm

2mm

2mm

2mm